Elghali M and Abdellaoui M
In this study, we report on the synthesis of a new AB3-type compound LaZr2Mn4Ni5 (with a content of 40 wt %) at room temperature during 5h of mechanical alloying. This compound was synthesized from the two binary compounds LaNi5 (CaCu5-type structure, P6/mmm space group) and ZrMn2-Laves phase (MgZn2-type structure, P63/mmc space group) in order to take advantage of the hydrogen absorption properties of these two types of intermetallic compounds. Structural properties were investigated using X-ray diffraction (XRD). The surface morphology of the cycled electrode was observed by a scanning electron microscope (SEM). The electrochemical properties of the LaZr2Mn4Ni5–based alloy were determined using the chrono-potentiometry method. The experimental results indicate that the discharge capacity reaches a maximum value of 300 mAh/g. Solid-gaz reaction shows that this compound is able to form the LaZr2Mn4Ni5H13 hydride at room temperature at an absorption plateau pressure of about 7 bar.